Effect of aluminium element on microstructure and properties of weld metal of 960 MPa steel

A kind of self-protective flux cored wire has been developed for joining 960 MPa high strength steel. Weld metal containing different aluminium elements contents was obtained by changing the content of aluminum powder in the composition of the flux core. The strength and toughness of weld metal were tested by tensile test and impact test at different temperatures, and the influence mechanism of aluminium element on the microstructure and mechanical properties of weld metal was analyzed by means of metallographic microstructure observation and scanning electron microscope observation. The results show that aluminium element content on impact ductility of weld metal of 960 MPa high strength steel is great, but the influence on tensile strength and elongation of weld metal is little. With increasing aluminium element contents of weld metal, the impact energy of weld metal increases at first and then decreases, the best aluminium element content of weld metal is 0.2 wt.%. Aluminium oxide is easy to be formed in weld metal with low aluminium element contents, and the aluminium oxide can easily become nucleation particle for acicular ferrite. It is conducive to formation more acicular ferrite and will improve impact absorbing energy of weld metal. Aluminium nitride will easily formed in weld metal with high aluminium element content, and the coarse ferrite microstructure appears in weld metal and reduces impact energy of weld metal.