Effect of W/Cu composite filler metals on the microstructure and mechanical properties of laser welded pure niobium/304 stainless steel joint

Cracking in a laser weld of niobium to stainless steel occurred due to the formation of brittle,continuously distributed Nb-Fe intermetallic compounds.A crack-free joint,which had a tensile strength of 147 MPa,was obtained by using the W/Cu composite filler metals.To determine the reasons for cracking in the Nb/SS joint and the function of the W/Cu composite filler metals on the improvement of the cracking resistance of the Nb/W/Cu/SS joint,the microstructures of the joints were studied by optical microscopy,scanning electron microscopy and X-ray diffraction.The cracking susceptibilities of the joints were evaluated with microhardness test on the cross section of the Nb/W/Cu/SS joint.The results showed that the Nb/W/Cu/SS joint was characterized by various solid solution.The formation of solid solution reduced the cracking susceptibility of the joint.